Effect of Solid/Liquid and Eutectic Front Velocities on Microstructure Evolution in Al-20%Cu Alloys

Abstract

During the solidification process, microstructures are affected by the experimental conditions, the thermophysical characteristics of the alloy, and the type of grain-refining particles. Unidirectional solidification experiments were performed in a vertical Bridgman-type furnace to investigate the effect of the solidification front velocity on the solidified microstructure of a non-refined and refined Al-20%Cu alloy. The samples were solidified by rapidly increasing the sample velocity (v) range from 0.02 mm/s to 0.2 mm/s while maintaining an almost constant temperature gradient (~5 K/mm). As a result, despite changes in the solid/liquid front velocity along the sample, the microstructure of the non-refined alloys remained columnar. In the refined alloy, the columnar structure changed into an equiaxed structure at two different front velocities.

Keywords

• Al-20%Cu
• columnar-to-equiaxed transition (CET)
• grain refinement
• unidirectional solidification
• Bridgman-type furnace