Synthesis of Silicon Carbide Powders from Methyl-Modified Silica Aerogels

Abstract

β-silicon carbide (SiC) powders were synthesized by the carbothermal reduction of methyl-modified silica aerogel/carbon mixtures. The correlations between the phase evolution and morphologies of the SiC powders and the C/SiO2 ratio were investigated. At a C/SiO2 ratio of 3, β-SiC formed at 1425 °C and single-phase SiC powders were obtained at 1525 °C. The methyl groups (-CH3) on the silica aerogel surfaces played important roles in the formation of SiC during the carbothermal reduction. SiC could be synthesized from the silica aerogel/carbon mixtures under lower temperature and C/SiO2 ratios than those needed for quartz or hydrophilic silica. The morphology of the SiC powder depended on the C/SiO2 ratio. A low C/SiO2 ratio resulted in β-SiC powder with spherical morphology, while agglomerates consisting of fine SiC particles were obtained at the C/SiO2 ratio of 3. High-purity SiC powder (99.95%) could be obtained with C/SiO2 = 0.5 and 3 at 1525 °C for 5 h.

Keywords

• silicon carbide (SiC)
• silica (SiO₂)
• aerogel
• surface methyl (-CH₃) group
• carbothermal reduction