Enhancement on Physicomechanical Properties of Short-Rotation Teak Woods by Non-Biocide Chemical and Thermal Treatments

Abstract

Lactic acid (LA), citric acid (CA), and glycerol (G) are renewable and environmentally friendly chemicals that could improve the qualities of short-rotation teak (SRT) woods. This study investigated the effect of thermal and chemical modification using 20% aqueous solutions (w/w) of LA, CA, and G and their mixtures in the same composition on physical and mechanical properties of SRT teak wood. The impregnation process was initiated by vacuum process for 1 h and pressure (12.2 bar) for 2 h, followed by thermal (150 °C) treatment for 6 h on the SRT wood samples after being removed from the vacuum-pressure tube. Retention (R), weight percent gain (WPG), density (D), anti-swelling efficiency (ASE), leachability (WL), modulus of elasticity (MOE), and modulus of rupture (MOR) were measured. FTIR spectrometry and SEM analyses were performed. The wood impregnated with a mixture of 10% LA + 10% CA provided the highest ASE values of 50.1%, and the lowest leaching resistance of 1.54%. Based on wood strengths (MOE and MOR) and physical properties, as well as supported by FTIR and SEM analysis, the use of 10% LA + 10% CA is the most prospective as an impregnant formula for SRT wood modification of this research.

Keywords

• thermal modification
• chemical modification
• dimensional stability
• strength
• short rotation teak