Abstract

Three new Metal-Organic Frameworks, containing mesitylene tribenzoic acid as a linker and zinc (1) or cadmium as metals (2,3), were synthesized through solvothermal reactions, using DMF/ethanol/water as solvents, at temperatures of 80 °C (structures 1 and 3) and 120 °C (structure 2). Following single-crystal X-ray diffraction, it was found that 1 and 3 crystallize in the P21/c and C2/c space groups and form 2D networks, while 2 crystallizes in the Fdd2 space group, forming a 3D network. All three frameworks, upon heating, were found to be stable up to 350 °C. N2 sorption isotherms revealed that 1 displays a BET area of 906 m2/g. Moreover, the porosity of this framework is still present after five cycles of sorption/desorption, with a reduction of 14% of the BET area, down to 784 m2/g, after the fifth cycle. The CO2 loading capacity of 1 was found to be 2.9 mmol/g at 0 °C.

Keywords

• metal-organic framework
• mesitylene tribenzoic acid
• nitrogen sorption