Core-Shell Sr₂CeO₄@SiO₂ Filled COC-Based Composites with Low Dielectric Loss for High-Frequency Substrates

Abstract

High-frequency communication equipment urgently needs substrate materials with lower dielectric loss, better heat dissipation, and higher stability, to ensure real-time low-loss and high-speed signal transmission. The core-shell structure of Sr2CeO4@SiO2 was prepared by the sol-gel method, and the modified powders with different volume contents were introduced into the cyclic olefin copolymer (COC) to prepare hydrocarbon resin-based composites. Due to the protective effect of the SiO2 shell, the stability of the powders is significantly improved, and the moisture barrier and corrosion resistance of the composites are enhanced, which is conducive to the normal operation of electronic equipment in harsh and complex environments. When the filler content is 20 vol%, the composite has a dielectric loss of 0.0023 at 10 GHz, a dielectric constant of 3.5, a thermal conductivity of 0.9 W·m−1·K−1, a water absorption of 0.32% and a coefficient of thermal expansion of 37.7 ppm/°C. The COC/Sr2CeO4@SiO2 composites exhibit excellent dielectric properties and thermal conductivity, while maintaining good moisture resistance and dimensional stability, which shows potential application prospects in the field of high-frequency substrates.

Keywords

• polymer composite
• dielectric loss
• thermal conductivity
• stability