Powder samples of ABO3 perovskite manganites with the composition Pr0.6Sr0.4MxMn1-xO3 (M=Fe, Co, or Ni, 0.00≤x≤0.25) were synthesized using the sol-gel method. X-ray diffraction analyses showed that all three sets of samples had a single phase with an orthorhombic structure. The magnetic moment, μobs, of the samples at 10 K, decreased slowly for x≤0.10, whereas μobs decreased rapidly for x≥0.10. The dependences of μobs on the doping level x for the three series of samples were fitted successfully. In the fitting process, Mn, Fe, Co, and Ni cations were assumed to be trivalent, and the magnetic moment directions of Fe3+, Co3+, and Ni3+ cations were assumed to be canted antiferromagnetically coupled with Mn3+ cations. The cant angle ϕ decreased with the increase in x for x≤0.10 for Fe- and Ni-doped (x≤0.15 for Co-doped) samples and increased rapidly when x≥0.10 (x≥0.15 for Co-doped) samples. These properties are discussed using an oxygen 2p itinerant electron model, which is very similar to the oxygen 2p hole model proposed by Alexandrov et al. [Phys. Rev. Lett. 96, 117003 (2006)].