Study of 13Cr-4Ni-(Mo) (F6NM) Steel Grade Heat Treatment for Maximum Hardness Control in Industrial Heats

Abstract

The standard NACE MR0175 (ISO 15156) requires a maximum hardness value of 23 HRC for 13Cr-4Ni-(Mo) steel grade for sour service, requiring a double tempering heat treatment at temperature in the range 648–691 °C for the first tempering and 593–621 °C for the second tempering. Difficulties in limiting alloy hardness after the tempering of forged mechanical components (F6NM) are often faced. Variables affecting the thermal behavior of 13Cr-4Ni-(Mo) during single and double tempering treatments have been studied by means of transmission electron microscopy (TEM) observations, X-ray diffraction measurements, dilatometry, and thermo-mechanical simulations. It has been found that relatively low Ac1 temperatures in this alloy induce the formation of austenite phase above 600 °C during tempering, and that the formed, reverted austenite tends to be unstable upon cooling, thus contributing to the increase of final hardness via transformation to virgin martensite. Therefore, it is necessary to increase the Ac1 temperature as much as possible to allow the tempering of martensite at the temperature range required by NACE without the detrimental formation of virgin martensite upon final cooling. Attempts to do so have been carried out by reducing both carbon (<0.02% C) and nitrogen (<100 ppm) levels. Results obtained herein show final hardness below NACE limits without an unacceptable loss of mechanical strength.

Keywords

• supermartensitic stainless steels
• tempering treatments
• austenite reversion