Hybrid superabsorbent polymer networks (SAPs) encapsulated with SiO2 for structural applications

Abstract

In this work, materials that as additives in cement promote self-sealing/healing properties by the gradual release of water they absorb were synthesized, characterized and evaluated. Specifically, hybrid SAPs that absorb high ammounts of water encapsulated with SiO2 that facilitates their incorporation in the matrix since it improves their chemical affinity were investigated. The structure and morphology of the fabricated SAPs were characterized analytically and confirmed the synthesis of P(MAA-co-EGDMA)@SiO2 nanocomposite. Its particle size is expected to reduce the size of the pores formed due to the absorbing/desorbing water process during the mixing and curing of cement. Moreover, the water absorbance of the above mentioned material as well as its ability to maintain its original structure during subsequent cycles of absorbing/desorbing water from different mediums and specifically from distilled water (DW) and cement slurry filtrate (CS) were evaluated. CS was chosen to mimic the cementitious environment considering the presence of various ions and its pH value (~ 12). The results revealed that the absorption ratio of P(MAA-co-EGDMA)@SiO2 in DW and CS was higher than 1500 wt.% its original dry weight, while SEM pictures proved that the hybrid SAPs maintained their structure after the water absorption tests.