Colloidal-chemistry based synthesis of quantized CuInS2/Se2 nanoparticles

Abstract

Ternary chalcogenide nanoparticles, CuInS2 and CuInSe2, were synthesized in high- temperature boiling organic non-polar solvent. The X-ray diffraction analysis revealed that both materials have tetragonal (chalcopyrite) crystal structure. Morphology of the obtained materials was revealed by using transmission electron microscopy. Agglomerated spherical CuInS2 nanoparticles with broad size distribution in the range from 2 to 20 nm were obtained. In the case of CuInSe2, isolated particles with spherical or prismatic shape in the size range from 10 to 25 nm were obtained, as well as agglomerates consisting of much smaller particles with diameter of about 2-5 nm. The particles with the smallest diameters of both materials exhibit quantum size effect.

Keywords

• I-III-VI2 semiconductors
• quantization
• X-ray diffraction
• optical properties