Boletín de la Sociedad Española de Cerámica y Vidrio (Jun 2000)
Procesado electroquímico de un polímero conductor: mimetismo con los metales
Abstract
When an anodic current density of 0.5 mA. cm-2 is applied during 60 s through acetonitrile solutions containing, 5 mM SNS + 0.1 M LiClO4, adherent and uniform poly(SNS) films are electrogenerated on a platinum electrode. These polymeric films can be electrodissolved in the background solution when a cathodic current density is applied. They can be also electrodeposited from solutions of the reduced polymer in the background solution by flow of an anodic current. In this work the influence of different electrolytes: tetraethylammonium perchlorate (TEAClO4), tetrabutylammonium perchlorate (TBAClO4) and tetrahexyl-ammonium perchlorate (THAClO4) in electrogeneration, electrodissolution and electro deposition processes has been studied.<br><br>Se ha demostrado que aplicando una densidad de corriente anódica de 0.5 mA. cm-2 a través de una disolución de acetonitrilo de concentración 5 mM en SNS y 0.1 M en LiClO4, se obtienen películas de poli(SNS) adherentes y uniformes sobre un electrodo de platino. Estas películas poliméricas pueden electrodisolverse (al aplicar una densidad de corriente catódica) y electrodepositarse (al oxidar las cadenas poliméricas que se encuentran reducidas y disueltas en la disolución de fondo). En este trabajo se ha estudiado la influencia de distintos electrolitos: tetraetilamonioperclorato (TEAClO4), tetrabutilamonioperclorato (TBAClO4) y tetrahexilamonioperclorato (THAClO4) en los procesos de electrogeneración, electrodisolución y electrodepósito.