Quasi-Static Penetration Properties of Hybrid Composites with Aramid, Carbon and Flax Fibers as Reinforcement

Abstract

This work presents the experimental results of a quasi-static penetration test of laminates on a polyurea-polyurethane matrix, reinforced with aramid, carbon and flax fibers. A total of 15 series of samples with different reinforcement configurations were prepared. A quasi-static penetration test was performed for coefficient: SPR=5. The SPR= Ds/Dp was calculated as the ratio of the support hole diameter (Ds) to the punch diameter (Dp). A punch with a rounded 9-mm diameter tip was used to penetrate the material. Percentage changes of penetration energy (%E) and maximum load (%P) compared to a non-hybrid laminate were calculated in order to estimate the impact of hybridization on the properties of laminates. The energy absorbed during the quasi-static penetration test was used to calculate the PSS (punch shear strength) of the laminates. Damage analysis was performed after the puncture test. It was observed that both the type of reinforcement and the configuration of the reinforcement layers have a potential impact on the obtained results and the laminate damage mechanism.

Keywords

• laminates
• hybridization
• hybrid composites
• polymer-matrix composites
• quasi-static penetration test