Intrinsic Dielectric Loss in Zr_0.8Sn_0.2TiO₄ Ceramics Investigated by Terahertz Time Domain Spectroscopy

Abstract

Terahertz time-domain spectroscopy (THz-TDS) was employed for estimation of intrinsic dielectric loss of Zr0.8Sn0.2TiO4 (ZST) ceramics. Single-phase ZST dielectric resonators (DRs) with various synthesis parameters and, consequently, different extrinsic losses, were prepared by conventional ceramic technology. Even though the DRs exhibit a similar microstructure, their quality factor (Q is the inverse of dielectric loss tangent) measured in microwave (MW) domain at 6 GHz varies between 2500 and 8400. On the other hand, it was found that the THz dielectric loss is less sensitive to the sample preparation. The intrinsic losses (Q × f ~60 THz) of the ZST ceramics have been derived from THz data.

Keywords

• electroceramics
• microwave dielectrics
• zirconium tin titanate
• dielectric resonators
• intrinsic loss
• terahertz time-domain spectroscopy