Nanosized Eu³⁺-Doped NaY₉Si₆O₂₆ Oxyapatite Phosphor: A Comprehensive Insight into Its Hydrothermal Synthesis and Structural, Morphological, Electronic, and Optical Properties

Abstract

Detailed analysis covered the optical and structural properties of Eu3+-doped NaY9Si6O26 oxyapatite phosphors, which were obtained via hydrothermal synthesis. X-ray diffraction patterns of NaY9Si6O26:xEu3+ (x = 0, 1, 5, 7, 10 mol% Eu3+) samples proved a single-phase hexagonal structure (P63/m (176) space group). Differential thermal analysis showed an exothermic peak at 995 °C attributed to the amorphous to crystalline transformation of NaY9Si6O26. Electron microscopy showed agglomerates composed of round-shaped nanoparticles ~53 nm in size. Room temperature photoluminescent emission spectra consisted of emission bands in the visible spectral region corresponding to 5D0 → 7FJ (J = 0, 1, 2, 3, 4) f-f transitions of Eu3+. Lifetime measurements showed that the Eu3+ concentration had no substantial effect on the rather long 5D0-level lifetime. The Eu3+ energy levels in the structure were determined using room-temperature excitation/emission spectra. Using the 7F1 manifold, the Nv-crystal field strength parameter was calculated to be 1442.65 cm−1. Structural, electronic, and optical properties were calculated to determine the band gap value, density of states, and index of refraction. The calculated direct band gap value was 4.665 eV (local density approximation) and 3.765 eV (general gradient approximation). Finally, the complete Judd–Ofelt analysis performed on all samples confirmed the experimental findings.

Keywords

• NaY₉Si₆O₂₆
• oxyapatite
• europium ions
• nanophosphors
• amorphous-to-crystalline transformation