Efecto de la estequiometría y de la temperatura de cocción en el desarrollo de la fase Al<sub>2</sub>TiO<sub>5</sub>
Abstract
Aluminum Titanate (Al2TiO5) due to its low termal expansion coefficient, low wettability and high refractoriness is a promissing refractory ceramic to be in contact with non ferrous metals, specially molten aluminum. Controlled amounts of CaO, SiO2, MgO and ZrO2 are normally added in order to avoid expontaneous decomposition, lower than 1300°C, into its constituint oxides. In this work through the adoption of a new approach, it was investigated the Al2TiO5 phase development and stabilization with respect to stoichiometry and firing temperature. It was found that an excess of Titania (TiO2) helps the development of a stable and purer Aluminum Titanate phase.El Titanato de Aluminio (Al2TiO5) debido a su bajo coeficiente de expansión térmica, elevada refractariedad y baja mojabilidad por metales no ferrosos fundidos, es un material prometedor en la industria del Aluminio para aplicaciones donde se exige contacto con el baño metálico. Aditivos como CaO, SiO2, MgO y ZrO2 son necesarios para evitar la descomposición espontánea del Al2TiO5 en sus óxidos constituyentes a temperaturas inferiores a 1300°C. En este trabajo, se ha investigado el efecto de la estequiometría y de la temperatura de sinterización en el desarrollo y estabilidad de la fase Al2TiO5. Se ha encontrado que un exceso de Óxido de Titanio (TiO2) es beneficioso en la producción de Al2TiO5 puro y estable.