Radiolytic Gas Production from Aluminum Coupons (Alloy 1100 and 6061) in Helium Environments—Assessing the Extended Storage of Aluminum Clad Spent Nuclear Fuel

Abstract

Corrosion of aluminium alloy clad nuclear fuel, during reactor operation and under subsequent wet storage conditions, promotes the formation of aluminium hydroxide and oxyhydroxide layers. These hydrated mineral phases and the chemisorbed and physisorbed waters on their surfaces are susceptible to radiation-induced processes that yield molecular hydrogen gas (H2), which has the potential to complicate the long-term storage and disposal of aluminium clad nuclear fuel through flammable and explosive gas mixture formation, alloy embrittlement, and pressurization. Here, we present a systematic study of the radiolytic formation of H2 from aluminium alloy 1100 (AA1100) and 6061 (AA6061) coupons in “dry” (~0% relative humidity) and “wet” (50% relative humidity) helium environments. Cobalt-60 gamma irradiation of both aluminium alloy types promoted the formation of H2, which increased linearly up to ~2 MGy, and afforded G-values of 1.1 ± 0.1 and 2.9 ± 0.1 for “dry” and “wet” AA1100, and 2.7 ± 0.1 and 1.7 ± 0.1 for “dry” and “wet” AA6061. The negative correlation of H2 production with relative humidity for AA6061 is in stark contrast to AA1100 and is attributed to differences in the extent of corrosion and varying amounts of adsorbed water in the two alloys, as characterized using optical profilometry, scanning electron microscopy, Raman spectroscopy, and X-ray diffraction techniques.

Keywords

• gamma radiolysis
• molecular hydrogen generation
• aluminum clad spent nuclear fuel