Novel Hybrid Electrode Coatings Based on Conjugated Polyacid Ternary Nanocomposites for Supercapacitor Applications

Abstract

Electrochemical behavior of novel electrode materials based on polydiphenylamine-2-carboxylic acid (PDPAC) binary and ternary nanocomposite coatings was studied for the first time. Nanocomposite materials were obtained in acidic or alkaline media using oxidative polymerization of diphenylamine-2-carboxylic acid (DPAC) in the presence of activated IR-pyrolyzed polyacrylonitrile (IR-PAN-a) only or IR-PAN-a and single-walled carbon nanotubes (SWCNT). Hybrid electrodes are electroactive layers of stable suspensions of IR-PAN-a/PDPAC and IR-PAN-a/SWCNT/PDPAC nanocomposites in formic acid (FA) formed on the flexible strips of anodized graphite foil (AGF). Specific capacitances of electrodes depend on the method for the production of electroactive coatings. Electrodes specific surface capacitances Cs reach 0.129 and 0.161 F∙cm−2 for AGF/IR-PAN-a/PDPACac and AGF/IR-PAN-a/SWCNT/PDPACac, while for AGF/IR-PAN-a/PDPACalk and AGF/IR-PAN-a/SWCNT/PDPACalk Cs amount to 0.135 and 0.151 F∙cm−2. Specific weight capacitances Cw of electrodes with ternary coatings reach 394, 283, 180 F∙g−1 (AGF/IR-PAN-a/SWCNT/PDPACac) and 361, 239, 142 F∙g−1 (AGF/IR-PAN-a/SWCNT/PDPACalk) at 0.5, 1.5, 3.0 mA·cm−2 in an aprotic electrolyte. Such hybrid electrodes with electroactive nanocomposite coatings are promising as a cathode material for SCs.

Keywords

• polydiphenylamine-2-carboxylic acid
• binary and ternary nanocomposites
• activated IR-pyrolyzed polyacrylonitrile
• single-walled carbon nanotubes
• hybrid electrode coatings
• organic electrolyte