State Key Laboratory of Optoelectronic Materials and Technologies, Guangdong Province Key Laboratory of Display Material and Technology, School of Electronics and Information Technology, Sun Yat-Sen University, Guangzhou 510275, China
Guofu Zhang
State Key Laboratory of Optoelectronic Materials and Technologies, Guangdong Province Key Laboratory of Display Material and Technology, School of Electronics and Information Technology, Sun Yat-Sen University, Guangzhou 510275, China
Yuan Xu
School of Biomedical Engineering, Southern Medical University, Guangzhou 510515, China
Yicong Chen
State Key Laboratory of Optoelectronic Materials and Technologies, Guangdong Province Key Laboratory of Display Material and Technology, School of Electronics and Information Technology, Sun Yat-Sen University, Guangzhou 510275, China
Shaozhi Deng
State Key Laboratory of Optoelectronic Materials and Technologies, Guangdong Province Key Laboratory of Display Material and Technology, School of Electronics and Information Technology, Sun Yat-Sen University, Guangzhou 510275, China
Jun Chen
State Key Laboratory of Optoelectronic Materials and Technologies, Guangdong Province Key Laboratory of Display Material and Technology, School of Electronics and Information Technology, Sun Yat-Sen University, Guangzhou 510275, China
A fully vacuum-sealed addressable flat-panel X-ray source based on ZnO nanowire field emitter arrays (FEAs) was fabricated. The device has a diode structure composed of cathode panel and anode panel. ZnO nanowire cold cathodes were prepared on strip electrodes on a cathode panel and Mo thin film strips were prepared on an anode panel acting as the target. Localized X-ray emission was realized by cross-addressing of cathode and anode electrodes. A radiation dose rate of 10.8 μGy/s was recorded at the anode voltage of 32 kV. The X-ray imaging of objects using different addressing scheme was obtained and the imaging results were analyzed. The results demonstrated the feasibility of achieving addressable flat-panel X-ray source using diode-structure for advanced X-ray imaging.