RuCo Alloy Nanoparticles Embedded into N-Doped Carbon for High Efficiency Hydrogen Evolution Electrocatalyst

Abstract

For large-scale and sustainable water electrolysis, it is of great significance to develop cheap and efficient electrocatalysts that can replace platinum. Currently, it is difficult for most catalysts to combine high activity and stability. To solve this problem, we use cobalt to regulate the electronic structure of ruthenium to achieve high activity, and use carbon matrix to protect alloy nanoparticles to achieve high stability. Herein, based on the zeolitic imidazolate frameworks (ZIFs), a novel hybrid composed of RuCo alloy nano-particles and N-doped carbon was prepared via a facile pyrolysis-displacement-sintering strategy. Due to the unique porous structure and multi-component synergy, the optimal RuCo500@NC750 material in both acidic and alkaline media exhibited eminent HER catalytic activity. Notably, the 3-RuCo500@NC750 obtained a current density of 10 mA cm−2 at 22 mV and 31 mV in 0.5 M H2SO4 and 1.0 M KOH, respectively, comparable to that of the reference Pt/C catalyst. Furthermore, the Tafel slopes of the catalyst are 52 mV Dec−1 and 47 mV Dec−1, respectively, under acid and alkali conditions, and the catalyst has good stability, indicating that it has broad application prospects in practical electrolytic systems. This work contributes to understanding the role of carbon-supported polymetallic alloy in the electrocatalytic hydrogen evolution process, and provides some inspiration for the development of a high efficiency hydrogen evolution catalyst.

Keywords

• electrocatalysis
• hydrogen evolution reaction (HER)
• water splitting
• hydrogen production
• RuCo alloy