Selective Leaching of Molybdenum from Bulk Concentrate by Electro-Oxidation

Abstract

This paper proposes selective leaching of molybdenum from Mo/Cu complex bulk concentrates in a 5 M NaCl solution using the electro-oxidation method. Here, the effects of several factors such as pH, pulp density, current density, and temperatures were investigated. A higher leaching yield of Mo increased with increasing pH from 5 to 9 and decreased with increasing pulp density from 1 to 10%. A rise in current density did not help enhance Mo, and the elevating temperature did not always result in a higher leaching yield. Application of ultrasonic led to higher leaching yield of Mo. Ninety-two percent of leaching yield was obtained upon leaching of Mo in 5 M NaCl at 25 °C, pulp density of 5%, and the current density of 0.292 A/g under ultrasonic irradiation with a power of 27 kW. The resultant residue mainly consisted of chalcopyrite.

Keywords

• electro-oxidation
• molybdenum
• selective leaching
• molybdenite
• chalcopyrite