Fabrication of Electroplated Nickel Composite Films Using Cellulose Nanofibers Introduced with Carboxy Groups as Co-Deposited Materials

Abstract

In this study, the fabrication of nickel (Ni)-cellulose nanofiber (CNF) composite electroplating films was attempted using sodium carboxymethyl cellulose (CMC) and 2,2,6,6-tetramethylpiperidine 1-oxyl (TEMPO)-oxidized CNF as CNF introduced with carboxy groups. As a result, co-deposition was confirmed for both CNFs, and the former showed 82% improvement in surface Vickers hardness compared to the plated film deposited from a conventional Watts bath without CNF. Although the latter showed slightly inferior 71% improvement, the surface roughness measurement showed a smoother surface than that of the plated copper material C1100. On the other hand, the film with CMC had a rough surface. The image analysis showed that the distance between co-deposited CNF on the surface of the plated film was 40% shorter on the specimen with TEMPO CNF than CMC, indicating that a fine dispersion was obtained. In addition, a co-deposition model was proposed in which Ni is deposited from the chelate complex formed between the carboxylate of CNF and Ni ions. CNF is fixed to the plated film surface by Ni deposition and the simultaneous bond of hydrogen ions to the carboxylate, resulting in a return to the carboxy group.

Keywords

• composite plating
• cellulose nanofiber
• electroplating
• codeposition mechanism
• composite material
• surface finishing