Adhesion Strength Enhancement of Butyl Rubber and Aluminum Using Nanoscale Self-Assembled Monolayers of Various Silane Coupling Agents for Vibration Damping Plates

Abstract

In this paper, we enhance the adhesion strength of butyl rubber-based vibrational damping plates using nanoscale self-assembled monolayers of various silane coupling agents. The silane coupling agents used to chemically modify the plate’s aluminum surface include 3-aminopropyltriethoxysilane (APTES), (3-glycidyloxypropyl) triethoxysilane (GPTES), 3-mercaptopropyltrimethoxysilane (MPTMS), and 3-(triethoxysilyl)propyl isocyanate (ICPTES). The modified surfaces were analyzed using Fourier transform infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS), and the enhancement in adhesion strength between the rubber and aluminum was estimated through T-Peel tests. As a result, MPTMS showed the highest enhancement in adhesion strength, of approximately 220% compared to the untreated sample, while GPTES, ICPTES, and APTES resulted in adhesion strength enhancements of approximately 200%, 150%, and 130%, respectively.

Keywords

• aluminum
• butyl rubber
• silane coupling agent
• self-assembly monolayer