Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 2006)
Degradación de recubrimientos ZrO<sub>2</sub>-CaO/NiAlMo por oxidación isoterma
Abstract
This paper analyses the degradation of a ceramic top coating 70%ZrO2 – 30%CaO deposited onto a stainless steel AISI 304 by thermal spray, using Ni-6%Al-5%Mo as overlay coating. These thermal barrier coatings were heat treated for 48, 120 and 288 h at 800 ºC to evaluate the degradation of these materials by isothermal oxidation. The microstructure evolution during oxidation was analysed by environmental scanning electron microscopy, transmission electron microscopy, X ray microanalysis and X ray diffraction. A thermally grown oxide layer was observed between the overlay coating and the ceramic top coating after oxidation. This layer was formed by a mixed Al and Ni oxides.En este trabajo se estudia la degradación de un recubrimiento 70%ZrO2 – 30%CaO crecido por proyección térmica de oxiacetileno sobre un acero inoxidable austenítico AISI 304 y empleando una leación de Ni-6%Al-5%Mo como capa de anclaje. Los recubrimientos se trataron térmicamente en aire a 800 ºC durante 48, 120 y 288 horas para evaluar la degradación de estos materiales por oxidación isotérmica. La evolución de la microestructura de las barreras como consecuencia del proceso de oxidación se analizó mediante microscopía electrónica de barrido ambiental, microscopía electrónica de transmisión, microanálisis de rayos X (EDX) y difracción de rayos X. Durante la oxidación de los recubrimientos creció una capa intermedia de óxidos (“thermally grown oxides”, TGO) entre el anclaje metálico y el recubrimiento cerámico formada por una mezcla de óxidos de Al y Ni.