Experimental Study on the Influence of Transverse Crack on Chloride Ingress in Concrete Slab Track of High-Speed Railway

Abstract

The concrete track slab and the base slab of the high-speed railway CRTS II track structure are prone to transverse cracks in the initial service period, which are subjected to environmental action and train load. In order to investigate the influence of transverse cracks on chloride ingress of concrete track slab and base slab in a coastal environment, drying-wetting cycle chloride erosion tests were carried out on reinforced concrete track slab and base slab specimens with cracks ranging from 0 mm to 0.6 mm, subjected to continuous bending moment. The chloride ion concentration of concrete along the depth direction was collected during the test process. The experimental results show that the chloride ion concentration of concrete at the crack section is much higher than that at the intact section, and it increases with the increase of crack width in the range of 0.2 mm to 0.6 mm. A chloride diffusion coefficient model of cracked concrete is proposed for slab track based on the experimental results, which can comprehensively consider the effects of surface chloride ion concentration, chloride binding effect, time-varying effect, temperature, relative humidity, and transverse crack width.

Keywords

• concrete slab
• slab track
• chloride diffusion
• transverse crack
• drying-wetting cycles
• durability