Preparation and application of profiled luminescent polyester fiber with reversible photochromism materials

Abstract

In this study, we realized a highly luminescent polyester fiber using a special spinneret orifice comprised of eight C-shaped pores and specific process parameters. A moderate amount of reversible photochromism materials was added along with the specific color masterbatch of suitable materials. With its high light transmittance and reflectance, the fabric has high glossiness and excellent transparency and exhibits dazzling color effects with changes in ambient light intensity. The raw materials used are polyethylene terephthalate (PET) chips with a low melting point of 110–150°C, 0.3–0.5% (active ingredient 30%) masterbatch, and 40–50% (active ingredient 50%) reversible photochromism masterbatch. The following process parameters were also chosen: for the PET chips, the drying temperature was 80–90°C, the drying time was 12–14 h, the masterbatch drying temperature was 70–80°C, the drying time was 8–10 h, the spinning temperature was 220–230°C, the cooling air temperature was 15–17°C, the cooling air speed was 0.45–0.50 m·min−1, the first hot roller temperature was 75–80°C, and the secondary hot roller had the heater turned off.

Keywords

• reversible photochromism
• profiled bright light
• colorful polyester
• preparation technology
• applied research