Effect of Nb on barium titanate prepared from citrate solutions

Abstract

The influence of the addition of dopants on the microstructure development and electrical properties of BaTiO3 doped with 0.2, 0.4, 0.6, 0.8 mol% of Nb and 0.01 mol% of Mn based compounds was studied. Doped barium titanate was prepared using the polymeric precursor method from citrate solutions. The powders calcined at 700°C for 4 hours were analysed by infrared (IR) spectroscopy to verify the presence of carbonates, and by X-ray diffraction (XRD) for phase formation. The phase composition, microstructure and dielectric properties show a strong dependence on the amount of added niobium.

Keywords

• organic precursor
• sintering
• microstructure
• dielectric properties
• BaTiO3
• Nb-doped