INVESTIGATION OF SORPTION CHARACTERISTICS OF POLYMERIC MINERAL-FILLED COMPOSITES FOR MEDICINE

Abstract

The polymer compositions on the base of acrylic derivatives and bentonite particles modified by silver ions with various share and dispersion are received and studied by radical polymerization in the water. Partially neutralized acrylic acid, acrylamide and methylene-bis-acrilamide and particles of bentonite with fraction 0 - 0,05 mass.% are chosen as initial substances. The influence of bentonite concentration on absorbing characteristics of polymer materials in the distilled water is shown. It is demonstrated that the increase of bentonite fraction up to 5 mass.% leads to the rise of degree of equilibrium swelling by 1,5 – 2 times in comparison with an unfilled polymer matrix. The acrylic nanocompositions with a mass fraction of bentonite equal to 0,01 mass.% possess the greatest kinetic characteristics. Kinetic dependences of new composite materials swelling in physiological solution from a filler dispersion part are investigated. It is shown that in high dispersion (with particle size less than 0,25 mm) a part of mineral–containing filler equal to 1 mass.% leads to significant increase in values of equilibrium swelling degree in comparison with an unfilled sample (by 1,5 times). The effect of polyelectrolyte suppression of polymer composition swelling in physiological solution is studied. It results in values reduction of equilibrium swelling degree in comparison with these values in the distilled water. Application prospects for the received compositions are shown at bandages creation for wounds treatment of various etiologies. Research results are recommended for usage in medical practice for optimization of wound process march.

Keywords

• cross-linked copolymers
• acrylic polymers
• hydro-gels
• swelling
• sorption
• bentonite
• silver