Covalently anchoring silver nanoclusters Ag44 on modified UiO-66-NH2 with Bi2S3 nanorods and MoS2 nanoparticles for exceptional solar wastewater treatment activity

Abstract

Abstract For the first time, covalently anchoring size selected silver nanoclusters [Ag44(MNBA)30] on the Bi2S3@UiO-66-NH2 and MoS2@UiO-66-NH2 heterojunctions were constructed as novel photocatalysts for photodegradation of methylene blue (MB) dye. The anchoring of Ag44 on MoS2@UiO-66-NH2 and Bi2S3@UiO-66-NH2 heterojunctions extended the light absorption of UiO-66-NH2 to the visible region and improved the transfer and separation of photogenerated charge carriers through the heterojunctions with a unique band gap structure. The UV–Vis-NIR diffuse reflectance spectroscopic analysis confirmed that the optical absorption properties of the UiO-66-NH2 were shifted from the UV region at 379 nm to the visible region at ~ 705 nm after its doping with Bi2S3 nanorods and Ag44 nanoclusters (Bi2S3@UiO-66-NH-S-Ag44). The prepared Bi2S3@UiO-66-NH-S-Ag44 and MoS2@UiO-66-NH-S-Ag44 photocatalysts exhibited exceptional photocatalytic activity for visible light degradation of MB dye. The photocatalysts exhibited complete decolorization of the MB solution (50 ppm) within 90 and 120 min stirring under visible light irradiation, respectively. The supper photocatalytic performance and recycling efficiency of the prepared photocatalysts attributed to the covalent anchoring of the ultra-small silver clusters (Ag44) on the heterojunctions surface. The X-ray photoelectron spectroscopic analysis confirmed the charge of the silver clusters is zero. The disappearance of the N–H bending vibration peak of primary amines in the FTIR analysis of Bi2S3@UiO-66-NH-S-Ag44 confirmed the covalent anchoring of the protected silver nanoclusters on the UiO-66-NH2 surface via the condensation reaction. The Bi2S3@UiO-66-NH-S-Ag44 catalyst exhibited excellent recyclability efficiency more than five cycles without significant loss in activity, indicating their good potential for industrial applications. The texture properties, crystallinity, phase composition, particle size, and structural morphology of the prepared photocatalysts were investigated using adsorption–desorption N2 isotherms, X-ray diffraction (XRD), HR-TEM, and FE-SEM, respectively.