Efficient quantum dot sensitized solar cells via improved loading amount management

Abstract

High light-harvesting efficiency and low interfacial charge transfer loss are essential for the fabrication of high-efficiency quantum dot-based solar cells (QDSCs). Increasing the thickness of mesoporous TiO2 films can improve the loading of pre-synthesized QDs on the film and enhance the absorbance of photoanode, but commonly accompanied by the increase in the unfavorable charge recombination due to prolonged electron transmission paths. Herein, we systematically studied the influence of the balance between QD loading and TiO2 film thickness on the performance of QDSCs. It is found that the relative thin photoanode prepared by the cationic surfactant-assisted multiple deposition procedure has achieved a high QD loading which is comparable to that of the thick photoanode commonly used. Under AM 1.5G illumination, Zn–Cu–In–Se and Zn–Cu–In–S based QDSCs with optimized 11.8 μm photoanodes show the PCE of 10.03% and 8.53%, respectively, which are comparable to the corresponding highest PCE of Zn–Cu–In–Se and Zn–Cu–In–S QDSCs (9.74% and 8.75%) with over 25.0 μm photoanodes. Similarly, an impressive PCE of 6.14% was obtained for the CdSe based QDSCs with a 4.1 μm photoanode, which is slightly lower than the best PCE (7.05%) of reference CdSe QDSCs with 18.1 μm photoanode.

Keywords

• Quantum dot sensitized solar cell
• Photoanode
• Loading amount
• Surfactant-assisted deposition