Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2004)
Fluencia a alta temperatura de policristales con tamaño de grano nanométrico de YTZP dopados con diferentes cantidades de fase vítrea
Abstract
Nano-sized YTZP (Yttria Tetragonal Zirconia Polycrystals) samples with different amounts of a glassy phase have been crept in a range of temperature between 1150ºC-1200ºC. A macroscopic characterization of the mechanical behaviour as well as the microstructural analysis by Transmission electron Microscopy (TEM) of both the as-received and deformed samples have been carried out. The glassy phase accounts for a significant softening while the deformation parameters values (n, Q) are not altered with respect to those measured in non-doped specimens of the same material with the same average grain size.Grain boundary sliding has been proved to be the deformation mechanism.<br><br>Muestras de YTZP (policristales de óxido de circonio dopados con itria) con tamaños de grano nanométrico y diferentes cantidades de fase vítrea han sido sometidas a experiencias de fluencia en un rango de temperatura entre 1150ºC y 1200ºC, con objeto de estudiar el comportamiento mecánico de dichos materiales. Para conocer los mecanismos de deformación puestos en juego se ha realizado el estudio microestructural de las muestras deformadas y no deformadas mediante Microscopía Electrónica de Transmisión (MET). Se ha demostrado que la presencia de fase vítrea da lugar a un significativo descenso de la resistencia a la fluencia. No obstante, los parámetros característicos de la deformación (n y Q) no se ven alterados, obteniéndose como mecanismo de deformación el deslizamiento de las fronteras de grano.