Comparison of the Grain-Refining Efficiencies of Ti and LaB₆ Inoculants in Additively Manufactured 2024 Aluminum Alloy: The Important Role of Solutes

Abstract

The present work aims to boost our understanding of factors governing the grain-refining efficiency of inoculation treatments by comparing the grain-refining efficiencies of two inoculators: Ti nanoparticles and LaB6 nanoparticles, in a 2024 Al alloy during additive manufacturing (AM). Experimental results obtained by scanning electron microscopy show that the LaB6 nanoparticle possessed almost no refining effect on the alloy, with the addition content ranging from 0.5 wt.% to 2 wt.%. Conversely, the Ti nanoparticle resulted in a more pronounced refinement and a fine, fully equiaxed microstructure at 1 wt.% Ti addition. Based on transmission electron microscopy analysis, the higher refining efficiency of Ti inoculation was ascribed to the incorporation of both Ti solute and the in situ-formed L12-Al3Ti nucleation particles. The former significantly increased the overall undercooling ahead of the growing Al grain, which ensured the activation of heterogeneous nucleation on the L12-Al3Ti nanoparticles, leading to grain refinement. This work highlights that despite the addition of nucleation particles, the incorporation of appropriate solutes to generate sufficient undercooling is the prerequisite for the activation of heterogenous nucleation in AM.

Keywords

• additive manufacturing
• aluminum alloys
• grain refinement
• EBSD
• TEM