Dimensional Stability and Mechanical Properties of <i>Gmelina arborea</i> Roxb. Wood Thermally Modified through Open Reactor and Low-Pressure Closed Reactor Systems

Abstract

This study focused on the thermal modification of Gmelina arborea Roxb. wood following processes using the open reactor and low-pressure closed reactor systems. The aim is to determine the optimum treatment conditions suitable for gmelina wood due to its poor drying characteristics using the low-pressure closed reactor thermal modification. Subsequent to thermal modification under both processes, the dimensional stability and mechanical properties of gmelina wood were investigated. Effects of the thermal modifications under the open and low-pressure closed reactor systems on mechanical properties were additionally reported. The outcome of this investigation revealed that mass loss increased with increasing treatment temperatures, but minimal mass losses were observed for samples modified in the low-pressure closed reactor system. Due to the low-pressure regime used in the closed reactor system, a lesser improvement was found in volumetric shrinkage, fibre saturation point and tangential-to-radial swelling compared to the improvement in these properties in the open reactor system. Results further revealed that the mechanical properties of gmelina wood deteriorated more rapidly after modification in the open reactor system. Since the properties of modified gmelina wood are comparable at 180 °C under both systems, the closed reactor system will be investigated further to arrive at a suitable treatment condition under higher pressure variations. The thermal modification of gmelina wood with the closed reactor system is more promising in delivering a better quality of modified gmelina wood.

Keywords

• thermal modification
• gmelina wood
• open reactor system
• closed reactor system
• volumetric swelling
• T/R ratio