High Temperature Dry Sliding Friction and Wear Performance of Laser Cladding WC/Ni Composite Coating

Abstract

Two different types of agglomerate and angular WC/Ni matrix composite coatings were deposited by laser cladding. The high temperature wear resistance of these composite coatings was tested with a ring-on-disc MMG-10 apparatus. The morphologies of the worn surfaces were observed using a scanning electron microscopy (SEM) equipped with an energy dispersive spectroscopy (EDS) for elemental composition. The results show that the high temperature wear resistance of the laser clad WC/Ni-based composite coatings is improved significantly with WC mass fraction increasing. The 60% agglomerate WC/Ni composite coating has optimal high temperature wear resistance. High temperature wear mechanism of 60% WC/Ni composite coating is from abrasive wear of low temperature into composite function of the oxidation wear and abrasive wear.

Keywords

• laser cladding
• composite coating
• tungsten carbide
• high temperature sliding dry friction
• wear resistance