Comparative retrieval analysis of antioxidant polyethylene: bonding of vitamin-E does not reduce in-vivo surface damage

Abstract

Abstract Background With the Persona® knee system a new polyethylene formulation incorporating vitamin-E which aims to reduce oxidation and maintain wear resistance was introduced. Although in-vitro studies have demonstrated positive effects of the vitamin-E antioxidants on UHMWPE, no retrieval study has looked at polyethylene damage of this system yet. It was the aim to investigate the in-vivo performance of this new design, by comparing it with its predecessor in retrieval analysis. Methods 15 NexGen® and 8 Persona® fixed-bearing implants from the same manufacturer (Zimmer Biomet) were retrieved from two knee revision centres. For retrieval analysis, a macroscopic analysis of polyethylene using a peer-reviewed damage grading method was used (Hood-score). The roughness of all articulating metal components was measured using a contact profilometer. The reason(s) for TKA revision were recorded. Statistical analyses (t-test) were performed to investigate differences between the two designs. Results The mean Hood score for Persona® inserts was 109.3 and for NexGen® 115.1 without significant differences between the two designs. Results from the profilometer revealed that Persona® and NexGen® femoral implants showed an identical mean surface roughness of 0.14 μm. The Persona® tibial tray showed a significantly smoother surface (0.06 μm) compared to the NexGen® (0.2 μm; p < 0.001). Both Hood score and surface roughness were influenced by the reasons for revision (p < 0.01). Conclusions The bonding of the antioxidant vitamin-E to the PE chain used in the novel Persona® knee system does not reduce in-vivo surface damage compared to highly crosslinked PE without supplemented vitamin-E used in its predecessor knee system NexGen®. However, the Persona® titanium alloy tibial tray showed a significantly smoother surface in comparison to the NexGen® titanium alloy tibial tray. This study provides first retrieval findings of a novel TKA design and may help to understand how the new Persona® anatomic knee system performs in vivo.

Keywords

• Total knee arthroplasty
• Polyethylene
• Retrieval analysis
• Polyethylene surface damage
• Surface roughness