e-Polymers (Jun 2023)
Preparation of (La + Nb)-co-doped TiO2 and its polyvinylidene difluoride composites with high dielectric constants
Abstract
Numerous studies have shown that ceramic materials with high dielectric constants and low dielectric losses can be obtained using donor–acceptor-doped TiO2. In this study, (La + Nb)-co-doped TiO2 [(La0.5Nb0.5)xTi1−x O2 x-LNTO] ceramic powders were prepared using the sol–gel method. XRD demonstrates that LNTO is a rutile phase, and the lattice parameters change after doping, while X-ray photoelectron spectroscopy explains the doping mechanism, with doping of TiO2 producing oxygen vacancies and Ti3+, which form defective dipoles with the dopant ions to increase the dielectric constant of the material. The dielectric properties were investigated by physically co-blending x-LNTO/polyvinylidene difluoride (PVDF) composites. Compared with the TiO2/PVDF composite, the dielectric properties of the x-LNTO/PVDF composite were more excellent. The dielectric constant of 5-LNTO/PVDF reached 36.96, which was higher than that of the TiO2/PVDF composite (19.49) at a filler addition of 60 wt% and a frequency of 1 kHz.
Keywords