InAs/InAsSb Strained-Layer Superlattice Mid-Wavelength Infrared Detector for High-Temperature Operation

Abstract

This paper reports an InAs/InAsSb strained-layer superlattice (SLS) mid-wavelength infrared detector and a focal plane array particularly suited for high-temperature operation. Utilizing the nBn architecture, the detector structure was grown by molecular beam epitaxy and consists of a 5.5 µm thick n-type SLS as the infrared-absorbing element. Through detailed characterization, it was found that the detector exhibits a cut-off wavelength of 5.5 um, a peak external quantum efficiency (without anti-reflection coating) of 56%, and a dark current of 3.4 × 10-4 A/cm2, which is a factor of 9 times Rule 07, at 160 K temperature. It was also found that the quantum efficiency increases with temperature and reaches ~56% at 140 K, which is probably due to the diffusion length being shorter than the absorber thickness at temperatures below 140 K. A 320 × 256 focal plane array was also fabricated and tested, revealing noise equivalent temperature difference of ~10 mK at 80 K with f/2.3 optics and 3 ms integration time. The overall performance indicates that these SLS detectors have the potential to reach the performance comparable to InSb detectors at temperatures higher than 80 K, enabling high-temperature operation.

Keywords

• infrared detector
• strained layer superlattice
• inas/inassb
• absorption coefficient
• barrier detector
• high operating temperature