Mechanochemical Characterisation of Calcined Impure Kaolinitic Clay as a Composite Binder in Cementitious Mortars

Abstract

The availability of some supplementary cementitious materials, especially fly ash, is of imminent concern in Europe due to the projected closure of several coal-fired power generation plants. Pure kaolinitic clays, which arguably have the potential to replace fly ash, are also scarce and expensive due to their use in other industrial applications. This paper examines the potential utilisation of low-grade kaolinitic clays for construction purposes. The clay sample was heat-treated at a temperature of 800 °C and evenly blended with Portland cement in substitutions of 10–30% by weight. The physical, chemical, mineralogical and mechanical characteristics of the blended calcined clay cement were determined. The Frattini test proved the pozzolanic potential of the calcined impure clay, as a plot of its CaO and OH− was found below the lime solubility curve. The 28 days compressive strengths trailed the reference cement by 5.1%, 12.3% and 21.7%, respectively, at all replacement levels. The optimum replacement level between the three blends was found to be 20 wt.%.

Keywords

• calcined clay
• supplementary cementitious materials
• low-grade kaolinitic clay
• compressive strength
• calcination