Influence of Exposure to Environment on Degradation of a Friction Stir Welded Aluminum Alloy

Abstract

We carried out a comparative study on both the stress corrosion response and corrosion damage characteristics of aluminum alloy 2219, both the base material and a friction stir welding (FSW) counterpart upon exposure to exfoliation corrosion (EXCO) solution. The results reveal that the test specimen containing an FSW joint reveals better electrochemical corrosion resistance than that taken from the base metal. When test specimens upon exposure to EXCO solution are concurrently subjected to a tensile stress, since the mechanical properties of the FSW joint are lower than the base metal, a test specimen containing an FSW joint is more easily prone to the early initiation of fine microscopic cracks. This makes the test specimen containing the FSW joint to be less resistant to stress corrosion damage than that taken from the base metal for the various levels of applied stress and exposure time to EXCO solution. The average corrosion depth of the test specimen containing the FSW joint is less than that of the base metal, while the maximum corrosion depth of it is greater than that of the base metal. This reveals that test specimen containing the FSW joint is more susceptible to damage and degradation than test specimen taken from the base metal.

Keywords

• aluminum alloy 2219
• FSW
• stress corrosion damage
• corrosion morphology