The Possibilities of Using Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) PHBV in the Production of Wood–Polymer Composites

Abstract

In this study, polymer biocomposites based on poly(3-hydroxybutyrate-co-3-hydroxyvalerate) PHBV biopolymers with Arbocel C350 SR wood fiber filler with mass contents of 15%, 30%, and 45% were described. Samples for testing were produced using the injection molding process. The shrinkage of the produced composites was determined, as well as the basic mechanical properties on the basis of the uniaxial static tensile test, hardness, and impact tensile test. The dimensional stability of samples was subject to temperature and humidity in the water absorption test. This research was carried out in terms of the problems with composite processing and use of products. This paper contains many remarks and conclusions regarding the processing and exploitation of the tested products, which can be extended to a larger range of cellulose fillers. It was found that it was possible to produce the tested type of composites with a content of up to 45 wt. of filler. However, the mechanical properties of the tested composites made it possible to use them for the production of selected products. These conclusions allow for conducting future research toward the effective use of WPC composites with a PHBV matrix and fibrous fillers of natural origin.

Keywords

• PHBV
• WPC
• PHBV–wood filler biocomposites
• polymer composites
• injection molding process