Crystal growth of K2TiGe3O9 in the glass

Abstract

The kinetics and mechanism of isothermal crystal growth of K2TiGe3O9 from a glass of the same stoichiometric composition were studied. The crystal growth rate U = 1 x 10-11-1.27 x 10-10 m s-1 was experimentally determined in the temperature interval of t = 540-600°C. In the range of high undercooling, Δt=435-375°C, spherical crystals growing at (374 ± 19) kJ mol-1 was observed.

Keywords

• Crystal growth
• K2TiGe3O9
• kinetics
• mechanism
• glass