Design and Rate Control of Large Titanium Alloy Springs for Aerospace Applications

Abstract

During the separation between satellite and launch vehicles, large steel springs are often used as compression separation spring sets in a catapult separation system. Replacing the steel springs with titanium alloy springs could reduce weight by about 50%. Although titanium alloy springs have been widely used in the aerospace field due to their excellent performance, there are few reports on the design of high-precision titanium alloy springs. The current spring design standards mainly focus on steel springs with helix angles between 5° and 9°, which are not applicable to titanium springs. Moreover, the change in spring rate with ambient temperature should also be considered. In this paper, β-C titanium alloy was used to design and prepare large compression separation springs, replacing steel springs in the catapult separation system. The design of titanium alloy springs took into account the big helix angle. The relationship between helix angle and the number of active coils was calculated. The parameters of titanium alloy springs were determined by the shear stress of the spring at working length. The effects of aging temperature and aging duration on the mechanical properties and modulus of β-C alloy were studied. By adjusting the aging process, the β-C alloy spring rate was controlled to meet the design requirements. The effect of ambient temperature on the mechanical properties and modulus of β-C titanium alloy were also investigated. It was found that as the ambient temperature increased, the rate of the β-C alloy spring gradually decreased.

Keywords

• titanium alloy spring
• spring rate
• helix angle
• elastic modulus
• shear modulus
• aging