Electromagnetic Shielding Effectiveness of Glass Fiber/Epoxy Laminated Composites with Multi-Scale Reinforcements

Abstract

In this study, an experimental investigation has been performed to understand the electromagnetic interference-shielding effectiveness (EMI-SE) of glass fiber/epoxy laminated composites embedded with carbon nanotubes (CNTs) and Fe3O4 nanoparticles, reinforced with micro carbon fibers along the thickness direction. Micro carbon fibers were reinforced along the thickness direction between the laminates using an electro-flocking process and a vacuum infusion process used to fabricate the composites. The EMI-SE of the composites was measured in the X-band frequency range (8–12 GHz). The effect of carbon fibers of three different lengths (80 µm, 150 µm, and 350 µm) with two different fiber densities (1000 and 2000 fibers/mm2) and two different amounts of Fe3O4 nanoparticles (0.5 and 1 wt.%) on total SE, absorption, and reflection was investigated. Due to the synergetic effect of Fe3O4 nanoparticles, CNTs, and carbon fibers, the final EMI shielding of the composites was mainly dominated by the absorption process. The absorption was more pronounced in the composites of longer carbon fibers with improved electrical conductivity. The presence of Fe3O4 nanoparticles also enhanced total SE values with improved magnetic permeability. The composite with micro carbon fibers of 350 µm length and 2000 fibers/mm2 density with 1 wt.% of Fe3O4 nanoparticles showed the maximum value of total SE.

Keywords

• electromagnetic shielding
• glass/epoxy composites
• carbon nanotubes
• carbon fibers
• iron oxide nanoparticles
• electro flocking