Fabrication and Characterizations of Hot-Melt Extruded Nanocomposites Based on Zinc Sulfate Monohydrate and Soluplus

Abstract

Zinc sulfate monohydrate (ZnSO4)-loaded nanocomposites (NCs) were fabricated by using a hot-melt extruder (HME) system. Soluplus (SP) was adopted as an amphiphilic polymer matrix for HME processing. The micro-size of ZnSO4 dispersion was reduced to nano-size by HME processing with the use of SP. ZnSO4 could be homogeneously dispersed in SP through HME processing. ZnSO4/SP NCs with a 75 nm mean diameter, a 0.1 polydispersity index, and a −1 mV zeta potential value were prepared. The physicochemical properties of ZnSO4/SP NCs and the existence of SP in ZnSO4/SP NCs were further investigated by solid-state studies. Nano-size range of ZnSO4/SP NC dispersion was maintained in the simulated gastrointestinal environments (pH 1.2 and 6.8 media). No severe toxicity in intestinal epithelium after oral administration of ZnSO4/SP NCs (at 100 mg/kg dose of ZnSO4, single dosing) was observed in rats. These results imply that developed ZnSO4/SP NC can be used as a promising nano-sized zinc supplement formulation. In addition, developed HME technology can be widely applied to fabricate nanoformulations of inorganic materials.

Keywords

• hot-melt extrusion
• nanocomposite
• Soluplus
• zinc sulfate monohydrate