Properties of Table Tennis Blade from Sorghum Bagasse Particleboard Bonded with Maleic Acid Adhesive at Different Pressing Temperatures and Times

Abstract

This physical and mechanical properties of a table tennis blade made from sorghum bagasse particleboard (TTBSB-particleboard) bonded maleic acid adhesive was investigated under pressing temperature and time variations. The TTBSB-particleboard was produced via a two-stage process in this study. A pressing temperature of 170–200 °C was used to prepare the first stage for 10 min. Following this, the second stage of the TTBSB-particleboard was produced with a different pressing time of 5–20 min. The TTBSB-particleboard had a specified target density of 0.6 g/cm3 and a size of 30 cm × 30 cm × 0.6 cm, respectively. For references concerning the tested quality of TTBSB-particleboard, the JIS A 5908-2003 standard has been used. For comparison, the commercial blades of Yuguan Wooden 1011 and Donic Original Carbo Speed were tested under the same conditions. The quality of the TTBSB-particleboard was successfully enhanced by increasing the pressing temperature (170 to 200 °C) and time (5 to 20 min). As a result, the pressing condition of 200 °C and 20 min were effective in this study. The TTBSB-particleboard in this study has a greater weight than the commercial blades of Yuguan and Donic. However, the TTBSB-particleboard in this study had a ball rebound comparable to that of the Donic blade.

Keywords

• maleic acid
• particleboard
• pressing temperature and time
• sorghum bagasse
• table tennis blade