ZrN-ZrO x N y vs ZrO2-ZrO x N y coatings deposited via unbalanced DC magnetron sputtering

Abstract

Abstract ZrN-ZrO $${ }_{x}$$ x N $${ }_{y}$$ y and ZrO $${ }_{2}$$ 2 -ZrO $${ }_{x}$$ x N $${ }_{y}$$ y coatings were deposited on 316L stainless steel substrates via the unbalanced DC magnetron sputtering technique in order to improve their corrosion resistance and evaluate their possible use as a coating biocompatible with bone cells. The composition, structure, morphology, and corrosion resistance were studied by sum means of x-ray photoelectron spectroscopy (XPS), x-Ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The corrosion resistance was evaluated in 3.5 wt.% NaCl using potentiodynamic polarization (PL) and electrochemical impedance techniques (EIS). The ZrN-ZrO $${ }_{x}$$ x N $${ }_{y}$$ y and ZrO $${ }_{2}$$ 2 -ZrO $${ }_{x}$$ x N $${ }_{y}$$ y coatings exhibited barrier-type protection of the substrate against corrosion. The growth of mouse osteoblast cells was evaluated in the coating that exhibited the greatest resistance to corrosion, ZrO $${ }_{2}$$ 2 -ZrO $${ }_{x}$$ x N $${ }_{y}$$ y , finding that the cell viability was maintained, so this material can be considered to be a candidate for use in osteosynthesis processes.