Unfilled Natural Rubber Compounds Containing Bio-Oil Cured with Different Curing Systems: A Comparative Study

Abstract

This study focuses on the properties of unfilled natural rubber compounds containing bio-oils cured with a peroxide curing system and then discusses the comparisons to those cured using the sulfur system from our previous work. Two types of bio-oils, i.e., palm oil and soybean oil, were used, and distillate aromatic extract (DAE)-based petroleum oil was employed as a reference. The bio-oils caused no significant change in the vulcanization of rubber compounds cured using peroxide. However, the compounds containing bio-oils and cured with sulfur showed a faster vulcanization than the ones with DAE. The bio-oils strongly affected the crosslink density of rubber compounds in both curing systems. The use of bio-oils caused a low crosslink density due to the possible implication of curing agents to bio-oil molecules. The properties of rubber compounds dependent on the different levels of crosslink density were also investigated. The results revealed that when the crosslink density increased, the modulus, tensile strength, and hardness of the rubber compounds increased and the elongation at break and compression set decreased. The use of bio-oils in the rubber compounds cured with different curing systems gave low modulus at 300% strain, tensile strength, and hardness but high elongation at break and compression set when compared to the ones with DAE. However, no significant change was observed for the compression set of the rubber compounds cured using sulfur. With the presence of bio-oils, the properties of rubber compounds cured with sulfur system deteriorated less than those of the ones cured with peroxide.

Keywords

• natural rubber
• processing oil
• bio-oil
• aromatic oil
• palm oil
• soybean oil