Boletín de la Sociedad Española de Cerámica y Vidrio (Dec 2002)
Effect of excess Mg and Excess Nb incorporation into the B-site of pyrochlore in the Pb-Mg-Nb-O system
Abstract
In the Pb-Mg-Nb-O system, excess Mg and excess Nb incorporation into the B-site of PMN pyrochlore were investigated along the compositons of Pb1.83Mg0.29+xNb1.71-xO6.39-1.5x where x=0.1, 0.2, 0.3, 0.4, 0.522 and Pb1.83Mg0.29-xNb1.71+xO6.39+1.5x where x=0.1, 0.2, 0.29 respectively. Excess Mg incorporation led to the formation of perovskite and excess Nb resulted in formation of Pb2Nb2O7 monoclinic pyrochlore. The densities of the PMN pyrochlore-PMN perovskite mixtures decreased with an increase in Mg concentration. The relative permittivity of the mixtures increased with decreasing pyrochlore content. The effect of pyrochlore on the permittivity follows the Weiner’s mixture rule up to a pyrochlore content of 50 vol%.<br><br>Se investigó la incorporación en lugares B de pirocloro PMN de un exceso de Mg y un exceso de Nb. En el sistema Pb-Mg-Nb-O2 las composiciones analizadas fueron Pb1.83Mg0.29+xNb1.71-xO6.39-1.5x donde x=0.1, 0.2, 0.3, 0.4, 0.522 y en Pb1.83Mg0.29-xNb1.71+xO6.39+1.5x donde x= 0.1, 0.2,0.29. El exceso de Mg condujo a la formación de perovskita y el exceso de Nb resultó en la formación del pirocloro monolínico, Pb2Nb2O7. La densidad de la mezcla de PMN pirocloro-perovskita dismunuye con el aumento de la concentración de Mg. La permitividad dieléctrica de las mezclas aumenta con la disminución del contenido de pirocloro. El efecto del pirocloro sobre la permitividad sigue la regla de mezclas de Weiner hasta conenidos de pirocloro del 50%.