Effect of Multi-Step Austempering Treatment on the Microstructure and Mechanical Properties of a High Silicon Carbide-Free Bainitic Steel with Bimodal Bainite Distribution

Abstract

The effect of multi-step austempering treatments on the microstructure and mechanical properties of a novel medium carbon high silicon carbide-free bainitic steel was studied. Five different isothermal treatment processes were selected, including single-step isothermal treatments above martensite start temperature (at 350 °C and 370 °C, respectively), and three kinds of two-step routes (370 °C + 300 °C, 370 °C + 250 °C, and 350 °C + 250 °C). In comparison with single-step austempering treatment adopting a two-step process, a microstructure with a bimodal-size distribution of bainitic ferrite and without martensite was obtained. Bainitic transformation was studied using dilatometry both for single-step and two-step routes and the specimens were completely characterised by electron microscopy (SEM and TEM), X-ray diffraction (XRD) and standard tensile tests. The mechanical response of the samples subjected to two-step routes was superior to those treated at a single temperature.

Keywords

• carbide-free bainite
• high silicon steel
• bimodal distribution
• multi-step austempering
• heat treatments