Polímeros (Jun 2008)
Dispersiones acuosas de poliuretano bloqueado: una alternativa como agente curtiente Aqueous dispersions of blocked polyurethane: an alternative as tanning agents
Abstract
Se sintetizaron y se evaluaron como agentes curtientes de pieles vacunas dos tipos de agentes de reticulación base poliuretano bloqueado. Se presentan los resultados de la síntesis de dispersiones acuosas de poliuretano bloqueado (DPU’s), basadas en prepolímeros a partir de la reacción de los diisocianatos alifáticos H12MDI (4,4’ metilenbis-ciclohexilisocianato) y HDI (hexametilendiisocianato) con polioles base poliéter óxido de etileno de peso molecular 1 y 2 KDa, en una relación molar isocianato/oxhidrilo (NCO/OH) de 4:1 y 6:1 a 100 °C por 2 y 4 horas. En una segunda reacción, los grupos isocianato (NCO) libres del prepolímero se bloquearon con una solución acuosa de NaHSO3 ó Na2S2O5 al 40%p/p. Los prepolímeros se caracterizaron mediante espectroscopia IR y RMN de ¹H. El tanto por ciento de isocianato libre en el prepolímero, así como el bloqueo de dichos grupos, se determinaron por espectroscopía IR. La evaluación de la capacidad curtiente de las DPU’s se determinó de acuerdo a la estabilidad térmica de la piel (temperatura de desnaturalización), mediante Calorimetría Diferencial de Barrido (DSC) y a la determinación del índice de reticulación de las DPU’s con la colágena de la piel mediante un ensayo con ninhidrina.Two types of crosslinking agents blocked polyurethanes were synthesized and evaluated as tanning agents of bovine skins. The results of the synthesis of aqueous dispersions of blocked polyurethane (DPU’s) are presented. They were based on prepolymers from the reaction of the aliphatic diisocyanates H12MDI 4,4’-methylenebis(cyclohexyl isocyanate) and HDI (hexamethylene diisocyanate) with HO-polyols such as polyethylene oxide of molecular weight 1 and 2 kDa. The molar NCO/OH ratio was fixed in 4:1 or 6:1, at 100 °C and 2 or 4 hours for the reaction time. In a second reaction, the prepolymer containing terminal NCO groups were blocked by reaction with an aqueous NaHSO3 or Na2S2O5 solution to 40% w/w. The obtained prepolymers were characterized by IR and ¹H NMR. The % of free isocyanate (NCO) in the prepolymer as well as the blockade of these groups were determined by IR. The evaluation of the tanning capacity of the DPU’s was determined according to the thermal stability of the skin (thermal denaturalization), through the differential scanning calorimetry analysis (DSC). The index of crosslinking of the DPU’s with the collagen of the skin was determined with the nynhidrin essay.
Keywords