Flexural and vibration behaviours of novel covered CFRP composite joints with an MWCNT-modified adhesive

Abstract

Co-curing bonding is more efficient than co-bonding and secondary bonding for structural component assembly. This work used novel covered laminas with co-cured joining techniques (CL-CCT) to create carbon fibre-reinforced polymer (CFRP) composite adhesive-bonded joints. Additionally, the researchers evaluated how multi-walled carbon nanotubes (MWCNTs) affect the bending and dynamic properties of CFRP composite joints. The researchers added various weights of MWCNTs to the covered laminas along with co-cured CFRP adhesive-bonded joints. The study revealed that epoxy and 0.25 wt% MWCNT adhesive produced the strongest and most flexible joints. These joints were 118 and 15% stronger than joints made from pure epoxy CL-CC CFRP, respectively. Compared to pure epoxy CC-CFRP composite joints, the strength of CL-CC CFRP composite joints with 0.25 wt% MWCNTs increased by 374 and 109%, respectively. Interestingly, MWCNTs with a wt% of 1.25 had the greatest natural frequency in all three vibration modes, which are 19, 19, and 13% higher than that of the pure epoxy CL-CC CFRP composite joint. There are 28, 30, and 24% more natural frequencies in 1.25 wt% MWCNT-based CL-CC CFRP composite joints than those in pure epoxy-based joints in all three modes. Analysis of variance was employed for statistical investigation. Optimization and prediction were done using an artificial neural network and the Levenberg–Marquardt technique.

Keywords

• cfrp composite joints
• covered laminas
• mwcnts
• anova
• and ann