Influence of incorporation of nanostructured silver vanadate decorated with silver nanoparticles on roughness, microhardness, and color change of pit and fissure sealants

Abstract

Objective: The aim of this study was to evaluate the roughness, hardness, and color change of pit and fissure sealants of two commercial brands (Fluroshield ™ and Ultraseal XT ™) incorporated with nanostructured silver vanadate nanomaterial decorated with silver nanoparticles (β-AgVO3) in concentrations (0% - control, 2.5% and 5%). Material and methods: Two commercial brands Fluroshield TM and Ultraseal XT ™ were used to make the samples with dimensions of 6 × 6 × 4 mm. The control group was made according to the manufacturer's instructions and in the groups with the addition of β-AgVO3, the nanomaterial was added proportionally by mass at percentages of 2.5% and 5%. Roughness properties were evaluated using a 3D Laser Confocal Microscope (n = 10), Knoop microhardness by Microdurometer (n = 10), and color change by Portable Color Spectrophotometer on the CIEDE2000 system (n = 10). Data were evaluated by one-way ANOVA with Bonferroni adjustment and Tukey's mean comparison test at a 5% significance level. Results: Ultraseal XT ™ sealant roughness showed a significant difference between concentrations with the highest mean for the 5% group (P = 0.010). Regarding the hardness, both sealants showed no significant difference between the groups. Fluroshield ™ sealant showed a significant difference in ΔE00 between the control-2.5% 24.93 (3.49) and control-5% 28.41 (2.58). Conclusion: It may be concluded that the incorporation of β-AgVO3 influenced the increase in roughness for Ultraseal XT ™ pit and fissure sealant, did not interfere with the microhardness of both sealants, and promoted a change in the color of Fluroshield ™ sealant within clinically acceptable limits.

Keywords

• Pit and fissure sealants
• Silver vanadate
• Color change
• Surface roughness
• Hardness